Study on bond behavior between steel bar and geopolymer concrete under freeze-thaw cycles
Author:
Affiliation:

Fund Project:

The National Natural Science Foundation of China (General Program, Key Program, Major Research Plan)

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    寒冷地区临海、盐碱土壤或冰盐环境中的混凝土结构因遭氯离子腐蚀和冻融循环的共同作用使得钢筋与混凝土间的黏结性能劣化,甚至会导致构件过早失效。为了分析在冻融循环和氯离子腐蚀耦合作用下地聚物混凝土与螺纹钢筋间黏结性能的变化规律,通过拉拔试验研究了地聚物混凝土与螺纹钢筋在此环境下的黏结性能,分析了保护层厚度(40 mm、60 mm、67 mm)、盐溶液浓度(0 %、5 %、10 %)和冻融次数(0次、15次、30次、50次)对极限黏结强度及黏结—滑移曲线的影响。结果表明:盐冻循环和水冻循环试件与未冻融试件破坏模式相同,均为劈裂破坏;但与未冻融的试件相比,极限黏结强度总体上降低,经过50次冻融循环后,盐冻和水冻试件的极限黏结强度为未冻融试件的56 %~67 %和80 %左右;最后,基于试验数据,提出考虑冻融次数和盐溶液浓度影响作用下地聚物混凝土劈裂抗拉强度以及极限黏结强度的拟合公式,以期为混凝土结构的工程应用提供理论参考。

    Abstract:

    Due to the combined action of chloride ion corrosion and freeze-thaw cycle, the bonding performance between steel bars and concrete will deteriorate, and even lead to premature failure of structures. In order to analyze the change law of bonding performance between geopolymer concrete and steel bars under the coupling action of freeze-thaw cycle and chloride ion corrosion, the bonding performance between geopolymer concrete and steel bars under this environment was studied by pull-out tests. The influences of the cover thickness of geopolymer concrete(40 mm、60 mm、67 mm), the concentration of salt solution(0 %、5 %、10 %)and the number of freeze-thaw cycles(0、15、30、50) on the ultimate bond strength and bond-slip curve of the specimens were analyzed. At the same time, the decaying rule of splitting tensile property of geopolymer concrete in deicer-frosting environment is summarized. The results show that the failure mode of the specimens in deicer-frosting cycles and water-freezing cycle is the same as that of the specimens without freeze-thaw cycle. However, the ultimate bond strength is generally lower than that of the without freezing specimens. After 50 freeze-thaw cycles, the ultimate bond strength of deicer-frosting cycle and water-freezing cycle specimens is about 56 %~67 % and 80 % of that of without freezing specimens. Finally, in order to providing reference for engineering application of concrete structures, a fitting formula for the splitting tensile strength and ultimate bond strength of geopolymer concrete considering the number of freeze-thaw cycles and salt solution concentration is proposed.

    参考文献
    相似文献
    引证文献
引用本文

邓芃,宋晓晓,张丽群,等. 冻融环境下地聚物混凝土和螺纹钢筋黏结性能的研究[J]. 科学技术与工程, 2022, 22(11): 4547-4555.
Deng Peng, Song Xiaoxiao, Zhang Liqun, et al. Study on bond behavior between steel bar and geopolymer concrete under freeze-thaw cycles[J]. Science Technology and Engineering,2022,22(11):4547-4555.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2021-07-18
  • 最后修改日期:2022-01-05
  • 录用日期:2021-11-30
  • 在线发布日期: 2022-04-20
  • 出版日期:
×
律回春渐,新元肇启|《科学技术与工程》编辑部恭祝新岁!
亟待确认版面费归属稿件,敬请作者关注