Effect of Electric Pulse Aging on Microstructure and Properties of Cu-2.5Fe-0.03P-0.1Zn Alloy
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    针对时效硬化型 Cu-2.5Fe-0.03P-0.1Zn 合金,采用微秒级高密度脉冲电流进行短时时效处理,试验研究了电脉冲处理对合金显微组织及硬度的影响。结果表明,适当参数的电脉冲时效,可使 Cu-2.5Fe-0.03P-0.1Zn 合金的析出相控制在细小的纳米尺度,从而使合金的电导率及显微硬度达到较理想的配合。

    Abstract:

    Microsecond high density electric pulse was used to shortly age Cu-2.5Fe-0.03P-0.1Zn copper alloy.The effects of electric pulse aging on the microstructures,electric conductivity and microhardness of this copper alloy were systematically investigated. The experimental results had shown that the alloy phase precipitated in Cu-2.5Fe-0.03P-0.1Zn alloy during electric pulse aging could be controlled to the order of fine nano-size and the ideal match of electric conductivity and microhardness could be achieved in the condition of optimized parameters of electric pulse.

    参考文献
    相似文献
    引证文献
引用本文

杨丽红 黄金亮 等. 电脉冲时效Cu—2.5Fe—0.03P—0.1Zn合金组织和性能[J]. 科学技术与工程, 2002, (6): 49-51.
YANG Lihong HUANG Jinliang YIN Biao. Effect of Electric Pulse Aging on Microstructure and Properties of Cu-2.5Fe-0.03P-0.1Zn Alloy[J]. Science Technology and Engineering,2002,(6):49-51.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:2002-08-21
  • 录用日期:
  • 在线发布日期:
  • 出版日期:
×
律回春渐,新元肇启|《科学技术与工程》编辑部恭祝新岁!
亟待确认版面费归属稿件,敬请作者关注