李兵,林煜期,王宏,等. 低坍落度聚丙烯纤维混凝土的高温后性能研究[J]. 科学技术与工程, 2021, 21(4): 1522-1528.
LI Bing,LIN Yu-qi,WANG Hong,et al.Study on the Properties of Low Slump Polypropylene Fiber Concrete After High Temperature[J].Science Technology and Engineering,2021,21(4):1522-1528.
低坍落度聚丙烯纤维混凝土的高温后性能研究
Study on the Properties of Low Slump Polypropylene Fiber Concrete After High Temperature
投稿时间:2020-04-23  修订日期:2020-05-28
DOI:
中文关键词:  低坍落度混凝土  聚丙烯纤维(PPF)  高温  微观结构  破坏机理  力学性能
英文关键词:low slump concrete  polypropylene fiber (PPF)  high temperature  microstructure  failure mechanism  mechanical property
基金项目:国家自然科学(51768017);海南省自然科学(20165189);海南大学科研启动项目(kyqd1566)
           
作者单位
李兵 海南大学 土木建筑工程学院
林煜期 海南大学 土木建筑工程学院
王宏 海南大学 土木建筑工程学院
董毓利 华侨大学 土木工程学院
摘要点击次数: 47
全文下载次数: 9
中文摘要:
      为探索PPF长度和掺量对低坍落度混凝土的影响,本文设计了171组基准混凝土和PPF混凝土标准立方体试块(150mm*150mm*150mm),并开展了常温下和高温后低坍落度混凝土的抗压强度试验和劈裂抗拉强度试验。基于试验结果给出了PPF对低坍落度混凝土抗压强度和劈裂抗拉强度的影响规律,并结合电镜扫描结果分析了低坍落度PPF混凝土的微观结构和破坏机理。结果表明:在适宜的长度和掺量范围下,PPF的掺入较明显改善高温前后的力学性能。同时在一定掺量下,发现PPF高温气化有助于混凝土的应力释放,提高了残余抗压强度。
英文摘要:
      In order to investigate the effects of PPF additions (length and content) to low slump concrete, the 171 groups of cube specimens (150mm*150mm*150mm) were designed, and their compressive strength and splitting tensile strength were tested under normal temperature and after different high temperatures. Based on large numbers of experiments, the mechanism of PPF to low slump concrete on compressive strength and splitting tensile strength was discussed. In the meantime, the SEM was used additionally to analyze the microstructure and failure mechanism of low slump PPF concrete. The results show that the mechanical properties of PPF before and after high temperature are obviously improved under the appropriate length and dosage range. And the high temperature gasification of PPF with a certain amount of admixture is helpful to the stress release of concrete and improve the residual compressive strength.
查看全文  查看/发表评论  下载PDF阅读器
关闭
你是第35589202位访问者
版权所有:科学技术与工程编辑部
主管:中国科学技术协会    主办:中国技术经济学会
Tel:(010)62118920 E-mail:stae@vip.163.com
京ICP备05035734号-4
技术支持:本系统由北京勤云科技发展有限公司设计

京公网安备 11010802029091号