Research on Surface Cleaning of NdFeB material by Nanosecond Pulsed Laser
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    利用激光清洗技术对钕铁硼材料进行清洗试验,探究不同激光功率对钕铁硼材料清洗效果的影响。通过SEM和EDS分析清洗后钕铁硼材料表面形貌及元素组成成分;利用白光干涉仪检测清洗后钕铁硼材料表面的粗糙度。结果表明,清洗后钕铁硼材料的表面粗糙度随着激光功率的增大先增大后减小随后又增大;激光功率较小时,钕铁硼材料表面存在烧蚀划痕和残留的腐蚀坑,表面C、O元素不能有效去除,清洗效果不佳;在激光功率为12 W,清洗后的材料表面光洁平整,无C、O元素,表面晶相组织完整清晰无破坏,说明此时激光清洗效果最佳;当激光功率更大时,超过材料的损伤阈值,表面出现微裂纹和细小的孔洞,清洗效果变差。

    Abstract:

    The cleaning experiment of NdFeB materials was carried out by laser cleaning technology, and the effects of different laser powers on the cleaning effect of NdFeB materials were investigated. The surface morphology and elemental composition of the NdFeB material after cleaning were analyzed by SEM and EDS. The surface roughness of the cleaned NdFeB material was measured by a white light interferometer. The results show that the surface roughness of the NdFeB material increases first and then decreases with the increase of laser power, and then increases. When the laser power is small, there are ablation scratches and residual corrosion Pit on the surface of NdFeB material. The surface C and O elements can not be effectively removed, cleaning effect is not good; when the laser power is 12 W, the surface of the material is smooth and clean after cleaning, without C and O elements, the surface crystal phase is clear and intact without damage, indicating the best laser cleaning effect at this time; when the laser power is larger, the damage threshold of the material is exceeded, micro-cracks and fine holes appear on the surface, and the cleaning effect is deteriorated.

    参考文献
    相似文献
    引证文献
引用本文

仝志宏,刘国东,黎相孟,等. 纳秒脉冲激光对钕铁硼材料表面清洗试验研究[J]. 科学技术与工程, 2020, 20(14): 5650-5655.
Tong Zhihong, Liu Guodong, Li Xiangmeng, et al. Research on Surface Cleaning of NdFeB material by Nanosecond Pulsed Laser[J]. Science Technology and Engineering,2020,20(14):5650-5655.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2019-08-22
  • 最后修改日期:2020-02-07
  • 录用日期:2019-11-17
  • 在线发布日期: 2020-06-11
  • 出版日期:
×
律回春渐,新元肇启|《科学技术与工程》编辑部恭祝新岁!
亟待确认版面费归属稿件,敬请作者关注